Silver Brazing alloys for carbide tungsten
Cadmium free Silver alloys for carbide tungsten are appreciated for excellent mechanical properties and bear good wetting characteristics. These are preferably used for brazing hard metals to steel mountings. Addition of nickel and manganese improves wettability on tungsten and molybdenum materials. Joint-brazing at working temperatures of max. 200 C without loss in strength. The above list is a standard range of our regular production, for any special request please do not hesitate to contact us directly or through our consultants.
Heat sources: acetylene torch, induction and resistance heating, vacuum furnace
Braze family of alloys is available in: wire, powder, paste, preforms, strip, ring and rods bare and flux coated
TO 425
Ag 25% Cu 38% Zn 33% Ni 2% Mn 2%
ISO3677: B-Cu38ZnAgNiMn-705/800
TO 427
Ag 27% Cu 38% Zn 20% Ni 5,5% Mn 9,5%
ISO3677: B-Cu38AgZnMnNi-680/830
TO 440
Ag 40% Cu 30% Zn 28% Ni 2%
ISO3677: B-Ag40CuZnNi-670/780
TO 449
Ag 49% Cu 16% Zn 23% Ni 4,5% Mn 7,5%
ISO3677: B-Ag49ZnCuMnNi-680/705
TO 450
Ag 50% Cu 20% Zn 28% Ni 2%
ISO3677: B-Ag50CuZnNi-660/705
TO 454
Ag 54% Cu 40% Zn 5% Ni 1%
ISO3677: B-Ag54CuZnNi-720/855
TO 456
Ag 56% Cu 42% Ni 2%
ISO3677: B-Ag56CuNi-770-895
TO 556
Ag 56% Cu 27% Ni 2,5% In 14,5%
ISO3677: B-Ag56CuNiIn-600/710
TO 564
Ag 64% Cu 26% Ni 2% Mn 2% In 6%
ISO3677: B-Ag64CuNiMnIn-730/780
TO 463
Ag 63% Cu 28,5% Ni 2,5% Sn 6%
ISO3677: B-Ag63CuSn-690/800
TO 485
Ag 85% Mn 15%
ISO3677: B-Ag85Mn-960/970
TO759
Ag 59% Cu 27,5% In 12,5% Ti 1,5%
ISO3677: B-Ag59CuInTi-605/715
TO770
Ag 70% Cu 26% Ti 4%
ISO3677: B-Ag70CuTi-780/900
TO 743
Ag 43,5% Cu 28% Ti 3% In 24,5%
ISO3677: B-Ag43,5CuTiIn-670/700
TO 760
Ag 60% Cu 24% Ti 2% In 14%
ISO3677: B-Ag60CuInTi-605/715